Mhlongo, Gugu HMotaung, DENkosi, SSSwart, HCMalgas, GFHillie, KTMwakikunga, Bonex W2014-09-222014-09-222014-02Mhlongo, G.H, Motaung, D.E, Nkosi, S.S, Swart, H.C, Malgas, G.F, Hillie, K.T and Mwakikunga, B.W. 2014. Temperature-dependence on the structural, optical, and paramagnetic properties of ZnO nanostructures. Applied Surface Science, vol. 293, pp 62-700169-4332http://ac.els-cdn.com/S0169433213023477/1-s2.0-S0169433213023477-main.pdf?_tid=994e45e8-3e4d-11e4-b7ef-00000aacb361&acdnat=1410946553_87d52090a94c676b6a3a7010ba6e3b78http://hdl.handle.net/10204/7688https://www.sciencedirect.com/science/article/pii/S0169433213023477https://doi.org/10.1016/j.apsusc.2013.12.076Copyright: 2014 Elsevier. This is an ABSTRACT ONLY. The definitive version is published in Applied Surface Science, vol. 293, pp 62-70Violet-blue emitting ZnO nanostructures were synthesized by a microwave-assisted hydrothermal method followed by post-synthesis annealing at different temperatures. Scanning electron microscope analysis revealed a morphological transformation upon increasing annealing temperature from well-defined “flower-like” structure composed of ZnO multi-nanorods to randomly oriented worm-like ZnO nanostructures. Raman analysis showed that the E(sub2) (high) mode became sharper and stronger while the intensity of the phonon peak at 580 cm(sup-1) was gradually enhanced with the increase of annealing temperature. X-ray diffraction and X-ray photoelectron spectroscopy (XPS) measurements showed that all ZnO samples possess a typical wurtzite structure with high crystallinity and no other impurity phases were observed. A decreasing trend in the photoluminescence (PL) intensity of a strong broad violet-blue emission from ZnO nanostructures with increasing annealing temperature was also observed. The electron spin resonance (ESR) signal was also found to gradually decrease with increasing annealing temperature indicating the decrease in the concentration of zinc interstitials (Zn(subi)) and/or zinc vacancies (V(subZn)) defects in ZnO nanostructures. Moreover, a combination of results from the PL, XPS and ESR suggested that Zn related defects; especially V(subZn) and Zn(subi) are the primary source of the paramagnetism observed in the ZnO nanostructures.enMicrowave-assisted synthesisZnO nanostructuresAnnealing effectsOptical propertiesMagnetic propertiesArticleMhlongo, G. H., Motaung, D., Nkosi, S., Swart, H., Malgas, G., Hillie, K., & Mwakikunga, B. W. (2014). Temperature-dependence on the structural, optical, and paramagnetic properties of ZnO nanostructures. http://hdl.handle.net/10204/7688Mhlongo, Gugu H, DE Motaung, SS Nkosi, HC Swart, GF Malgas, KT Hillie, and Bonex W Mwakikunga "Temperature-dependence on the structural, optical, and paramagnetic properties of ZnO nanostructures." (2014) http://hdl.handle.net/10204/7688Mhlongo GH, Motaung D, Nkosi S, Swart H, Malgas G, Hillie K, et al. Temperature-dependence on the structural, optical, and paramagnetic properties of ZnO nanostructures. 2014; http://hdl.handle.net/10204/7688.TY - Article AU - Mhlongo, Gugu H AU - Motaung, DE AU - Nkosi, SS AU - Swart, HC AU - Malgas, GF AU - Hillie, KT AU - Mwakikunga, Bonex W AB - Violet-blue emitting ZnO nanostructures were synthesized by a microwave-assisted hydrothermal method followed by post-synthesis annealing at different temperatures. Scanning electron microscope analysis revealed a morphological transformation upon increasing annealing temperature from well-defined “flower-like” structure composed of ZnO multi-nanorods to randomly oriented worm-like ZnO nanostructures. Raman analysis showed that the E(sub2) (high) mode became sharper and stronger while the intensity of the phonon peak at 580 cm(sup-1) was gradually enhanced with the increase of annealing temperature. X-ray diffraction and X-ray photoelectron spectroscopy (XPS) measurements showed that all ZnO samples possess a typical wurtzite structure with high crystallinity and no other impurity phases were observed. A decreasing trend in the photoluminescence (PL) intensity of a strong broad violet-blue emission from ZnO nanostructures with increasing annealing temperature was also observed. The electron spin resonance (ESR) signal was also found to gradually decrease with increasing annealing temperature indicating the decrease in the concentration of zinc interstitials (Zn(subi)) and/or zinc vacancies (V(subZn)) defects in ZnO nanostructures. Moreover, a combination of results from the PL, XPS and ESR suggested that Zn related defects; especially V(subZn) and Zn(subi) are the primary source of the paramagnetism observed in the ZnO nanostructures. DA - 2014-02 DB - ResearchSpace DP - CSIR KW - Microwave-assisted synthesis KW - ZnO nanostructures KW - Annealing effects KW - Optical properties KW - Magnetic properties LK - https://researchspace.csir.co.za PY - 2014 SM - 0169-4332 T1 - Temperature-dependence on the structural, optical, and paramagnetic properties of ZnO nanostructures TI - Temperature-dependence on the structural, optical, and paramagnetic properties of ZnO nanostructures UR - http://hdl.handle.net/10204/7688 ER -