Chakraborty, ASingh, JKSen, DPityana, Sisa LManna, IKrishna, SDutta Majumdar, J2021-01-172021-01-172020-09Chakraborty, A. et al. 2020. Microstructures, wear and corrosion resistance of laser composite surfaced austenitic stainless steel (AISI 304 SS) with tungsten carbide. Optics and Laser Technology, vol. 134, pp. 120030-39921879-2545https://www.sciencedirect.com/science/article/pii/S0030399220312184doi.org/10.1016/j.optlastec.2020.106585http://hdl.handle.net/10204/11722Copyright: 2020 Elsevier. Due to copyright restrictions, the attached PDF file only contains the abstract of the full text item. For access to the full text item, please consult the publisher's website. The definitive version of the work is published in Optics and Laser Technology, vol. 134, pp. 12This study aims at the development of composite surface on austenitic stainless (AISI 304 stainless steel) by laser surface alloying with WC and Co in the weight ratio of 4:1. Laser processing has been carried out by laser melting of sandblasted AISI 304SS using a 5 kW continuous-wave Nd: YAG laser having a beam diameter of 3 mm and simultaneous addition of powder (WC and Co in the ratio of 4:1) at a rate of 10 mg/sec using He as shroud (at a flow rate of 6 l/min) in the melted surface. The process parameters are applied power (1.75–2 kW) and scan speed (12–30 mm/sec) with a powder feed rate of 10 mg/s. The laser-treated surface has been subjected to microstructural investigation and wear resistance (fretting wear behaviour) testing. There is formation of different carbides (WC, W2C, Fe7C3, Cr23C6, Fe6W6C, and Co6W6C) in the gamma matrix of the treated zone. The microhardness of composite surface is significantly higher (980 VHN) than that of AISI 304SS (242 VHN). The fretting wear kinetics and coefficient of friction (COF) of the composite surface are reduced as compared to the substrate. The mechanism of wear has been established.enLaser surface treatmentsX-ray diffractionMicrohardnessArticleChakraborty, A., Singh, J., Sen, D., Pityana, S. L., Manna, I., Krishna, S., & Dutta Majumdar, J. (2020). Microstructures, wear and corrosion resistance of laser composite surfaced austenitic stainless steel (AISI 304 SS) with tungsten carbide. http://hdl.handle.net/10204/11722Chakraborty, A, JK Singh, D Sen, Sisa L Pityana, I Manna, S Krishna, and J Dutta Majumdar "Microstructures, wear and corrosion resistance of laser composite surfaced austenitic stainless steel (AISI 304 SS) with tungsten carbide." (2020) http://hdl.handle.net/10204/11722Chakraborty A, Singh J, Sen D, Pityana SL, Manna I, Krishna S, et al. Microstructures, wear and corrosion resistance of laser composite surfaced austenitic stainless steel (AISI 304 SS) with tungsten carbide. 2020; http://hdl.handle.net/10204/11722.TY - Article AU - Chakraborty, A AU - Singh, JK AU - Sen, D AU - Pityana, Sisa L AU - Manna, I AU - Krishna, S AU - Dutta Majumdar, J AB - This study aims at the development of composite surface on austenitic stainless (AISI 304 stainless steel) by laser surface alloying with WC and Co in the weight ratio of 4:1. Laser processing has been carried out by laser melting of sandblasted AISI 304SS using a 5 kW continuous-wave Nd: YAG laser having a beam diameter of 3 mm and simultaneous addition of powder (WC and Co in the ratio of 4:1) at a rate of 10 mg/sec using He as shroud (at a flow rate of 6 l/min) in the melted surface. The process parameters are applied power (1.75–2 kW) and scan speed (12–30 mm/sec) with a powder feed rate of 10 mg/s. The laser-treated surface has been subjected to microstructural investigation and wear resistance (fretting wear behaviour) testing. There is formation of different carbides (WC, W2C, Fe7C3, Cr23C6, Fe6W6C, and Co6W6C) in the gamma matrix of the treated zone. The microhardness of composite surface is significantly higher (980 VHN) than that of AISI 304SS (242 VHN). The fretting wear kinetics and coefficient of friction (COF) of the composite surface are reduced as compared to the substrate. The mechanism of wear has been established. DA - 2020-09 DB - ResearchSpace DP - CSIR KW - Laser surface treatments KW - X-ray diffraction KW - Microhardness LK - https://researchspace.csir.co.za PY - 2020 SM - 0030-3992 SM - 1879-2545 T1 - Microstructures, wear and corrosion resistance of laser composite surfaced austenitic stainless steel (AISI 304 SS) with tungsten carbide TI - Microstructures, wear and corrosion resistance of laser composite surfaced austenitic stainless steel (AISI 304 SS) with tungsten carbide UR - http://hdl.handle.net/10204/11722 ER -