Moller, HGovender, GStumpf, WEPistorius, PC2010-01-122010-01-122010Moller, H, Govender, G et al. 2010. Comparison of heat treatment response of semisolid metal processed alloys A356 and F357. International Journal of Cast Metals Research, Vol.23(1), pp 37-431364-0461http://hdl.handle.net/10204/3883Copyright: 2010 Maney PublishingThe heat treatment response of semisolid metal high pressure die cast Al-7Si-Mg alloys A356 and F357 was studied and compared. It was found that the heat treatment behaviour of alloy F357 is influenced markedly by the stability of the Mg containing p phase. This phase, which dissolves in alloy A356 during solution treatment, persists in F357 and decreases the amount of magnesium in solid solution. This is the likely origin of the decrease in the aging response of the F357 alloy. The tensile properties (yield strength and ultimate tensile strength) of the alloys correlate much better with the Mg concentration in solid solution than with the bulk Mg content of the alloys. The recently developed shortened T6 heat treatment cycles for rheocast A356 were tested on alloy F357. The optimum artificial aging treatment was determined to be 180uC for 4 h, regardless of the prior natural aging period.enSemisolid metal formingAlloy A356Alloy F357Artificial agingIron rich intermetallicsAlloysT6 heat treatmentArticleMoller, H., Govender, G., Stumpf, W., & Pistorius, P. (2010). Comparison of heat treatment response of semisolid metal processed alloys A356 and F357. http://hdl.handle.net/10204/3883Moller, H, G Govender, WE Stumpf, and PC Pistorius "Comparison of heat treatment response of semisolid metal processed alloys A356 and F357." (2010) http://hdl.handle.net/10204/3883Moller H, Govender G, Stumpf W, Pistorius P. Comparison of heat treatment response of semisolid metal processed alloys A356 and F357. 2010; http://hdl.handle.net/10204/3883.TY - Article AU - Moller, H AU - Govender, G AU - Stumpf, WE AU - Pistorius, PC AB - The heat treatment response of semisolid metal high pressure die cast Al-7Si-Mg alloys A356 and F357 was studied and compared. It was found that the heat treatment behaviour of alloy F357 is influenced markedly by the stability of the Mg containing p phase. This phase, which dissolves in alloy A356 during solution treatment, persists in F357 and decreases the amount of magnesium in solid solution. This is the likely origin of the decrease in the aging response of the F357 alloy. The tensile properties (yield strength and ultimate tensile strength) of the alloys correlate much better with the Mg concentration in solid solution than with the bulk Mg content of the alloys. The recently developed shortened T6 heat treatment cycles for rheocast A356 were tested on alloy F357. The optimum artificial aging treatment was determined to be 180uC for 4 h, regardless of the prior natural aging period. DA - 2010 DB - ResearchSpace DP - CSIR KW - Semisolid metal forming KW - Alloy A356 KW - Alloy F357 KW - Artificial aging KW - Iron rich intermetallics KW - Alloys KW - T6 heat treatment LK - https://researchspace.csir.co.za PY - 2010 SM - 1364-0461 T1 - Comparison of heat treatment response of semisolid metal processed alloys A356 and F357 TI - Comparison of heat treatment response of semisolid metal processed alloys A356 and F357 UR - http://hdl.handle.net/10204/3883 ER -