Mabhali, Luyolo ABPityana, Sisa LSacks, N2014-01-202014-01-202013-08Mabhali, L.A.B,, Pityana, S and Sacks, N. 2013. Impact toughness of laser alloyed aluminium AA1200 alloys. International Journal of Engineering and Technology Research, vol. 1(7), pp 127-1352327-0349http://www.ijeatr.org/IJEATR.org/IJEATR_Vol.%201,%20No.%207,%20August%202013/Impact%20toughness.pdfhttp://hdl.handle.net/10204/7157Copyright: IJEATR: International Journal of Engineering and Technology Research, vol. 1(7), pp 127-135Laser surface alloying of aluminium AA1200 was performed with a 4kW Nd:YAG laser and impact resistance of the alloys was investigated. The alloying powders were a mixture of Ni, Ti and SiC in different proportions. Surfaces reinforced with intermetallic phases and metal matrix composites were achieved during laser alloying. Brittle fracture of the SiC particles and transgranular cracking of the intermetallic phases was observed for the laser alloyed samples, while ductile fracture was observed for the bulk aluminium. Aluminium AA1200 metal absorbed high energy during fracture compared to laser alloyed samples due to its high ductility. Laser alloyed layers with a high Ti content had high absorbed energies which represent a reduction in brittleness, while alloyed layers with a high Ni content had low absorbed energies which indicate a preference for brittle fracture.enAluminium AA1200Laser alloyingImpact testTransgranular fractureIntermetallic phasesArticleMabhali, L. A., Pityana, S. L., & Sacks, N. (2013). Impact toughness of laser alloyed aluminium AA1200 alloys. http://hdl.handle.net/10204/7157Mabhali, Luyolo AB, Sisa L Pityana, and N Sacks "Impact toughness of laser alloyed aluminium AA1200 alloys." (2013) http://hdl.handle.net/10204/7157Mabhali LA, Pityana SL, Sacks N. Impact toughness of laser alloyed aluminium AA1200 alloys. 2013; http://hdl.handle.net/10204/7157.TY - Article AU - Mabhali, Luyolo AB AU - Pityana, Sisa L AU - Sacks, N AB - Laser surface alloying of aluminium AA1200 was performed with a 4kW Nd:YAG laser and impact resistance of the alloys was investigated. The alloying powders were a mixture of Ni, Ti and SiC in different proportions. Surfaces reinforced with intermetallic phases and metal matrix composites were achieved during laser alloying. Brittle fracture of the SiC particles and transgranular cracking of the intermetallic phases was observed for the laser alloyed samples, while ductile fracture was observed for the bulk aluminium. Aluminium AA1200 metal absorbed high energy during fracture compared to laser alloyed samples due to its high ductility. Laser alloyed layers with a high Ti content had high absorbed energies which represent a reduction in brittleness, while alloyed layers with a high Ni content had low absorbed energies which indicate a preference for brittle fracture. DA - 2013-08 DB - ResearchSpace DP - CSIR KW - Aluminium AA1200 KW - Laser alloying KW - Impact test KW - Transgranular fracture KW - Intermetallic phases LK - https://researchspace.csir.co.za PY - 2013 SM - 2327-0349 T1 - Impact toughness of laser alloyed aluminium AA1200 alloys TI - Impact toughness of laser alloyed aluminium AA1200 alloys UR - http://hdl.handle.net/10204/7157 ER -